20Cr無縫鋼管量大價(jia)廉

　　20Cr無(wu)縫鋼(gang)管，20Cr為珠光體，是可(ke)以(yi)進行焊接的，20Cr鋼(gang)焊接性較好，焊后(hou)一般不需(xu)熱處理。

　　20Cr無縫鋼(gang)管(guan)(guan)具(ju)有中空截面，大(da)量(liang)用(yong)作輸(shu)送(song)流體(ti)的管(guan)(guan)道(dao)，如(ru)輸(shu)送(song)石(shi)油、天然氣、煤氣、水及某些固(gu)體(ti)物(wu)料等。與(yu)圓(yuan)鋼(gang)等實(shi)心鋼(gang)材(cai)相比，在(zai)抗彎抗扭強度相同時，重量(liang)較輕，20Cr無縫鋼(gang)管(guan)(guan)是(shi)(shi)一種(zhong)經濟截面鋼(gang)材(cai)，廣(guang)泛用(yong)于制(zhi)(zhi)造結構件和(he)(he)機械零(ling)件，如(ru)石(shi)油鉆桿、汽車傳動軸、自行(xing)車架以及建筑(zhu)施工(gong)中用(yong)的鋼(gang)腳手架等。用(yong)20Cr鋼(gang)管(guan)(guan)制(zhi)(zhi)造環(huan)(huan)形(xing)(xing)零(ling)件，可(ke)提高材(cai)料利(li)用(yong)率，簡化(hua)制(zhi)(zhi)造工(gong)序，節約材(cai)料和(he)(he)加工(gong)工(gong)時，如(ru)滾動軸承套圈、千(qian)斤頂套等，目前已廣(guang)泛用(yong)鋼(gang)管(guan)(guan)來制(zhi)(zhi)造。20Cr無縫鋼(gang)管(guan)(guan)還是(shi)(shi)各(ge)種(zhong)常規武器不(bu)可(ke)缺少的材(cai)料，槍(qiang)管(guan)(guan)、炮筒等都要(yao)鋼(gang)管(guan)(guan)來制(zhi)(zhi)造。20Cr鋼(gang)管(guan)(guan)按橫截面積形(xing)(xing)狀的不(bu)同可(ke)分為圓(yuan)管(guan)(guan)和(he)(he)異(yi)型(xing)管(guan)(guan)。由于在(zai)周長相等的條件下，圓(yuan)面積最大(da)，用(yong)圓(yuan)形(xing)(xing)管(guan)(guan)可(ke)以輸(shu)送(song)更多(duo)的流體(ti)。此外，圓(yuan)環(huan)(huan)截面在(zai)承受內(nei)部(bu)或外部(bu)徑向(xiang)壓力(li)時，受力(li)較均勻，因此，絕大(da)多(duo)數鋼(gang)管(guan)(guan)是(shi)(shi)圓(yuan)形(xing)(xing)管(guan)(guan)材(cai)。

　　化學成份(%)：硅：0.17～0.37

　　力學(xue)性能：抗拉(la)強(qiang)度(du)(du) σb (MPa)：≥835屈(qu)服強(qiang)度(du)(du) σs (MPa)：≥540伸長(chang)率(lv) δ5 (%)：≥10斷面收縮率(lv) ψ (%)：≥40，沖擊吸收功Ak(J)≥47硬度(du)(du)：退火或(huo)高溫(wen)回火供應狀態(tai)硬度(du)(du)≤156HB，試(shi)樣(yang)尺(chi)寸：試(shi)樣(yang)尺(chi)寸15mm

　　熱處理規(gui)范及(ji)金相組(zu)織：

　　熱處理(li)規范(fan)：淬火(huo)溫度(du)(du)(℃)第一次880,第二次780～820，冷卻劑水(shui)和油。回火(huo)溫度(du)(du)(℃)200，冷卻劑水(shui)、空(kong)。

　　焊接性能：

　　2、厚(hou)度大于15mm的20Cr零件(jian)在焊前需預(yu)熱(re)到100～150℃，若要求不(bu)高焊前可不(bu)預(yu)熱(re)，焊后也可不(bu)進行回火熱(re)處理。